Analisis Pengaruh Variasi PH Larutan Acid Zinc Pada Sel Volta Dua Kompartemen dengan Elektrode Cu(Ag)-Zn

Authors

  • Gurum Ahmad Pauzi University of Lampung
  • Nilla Anggi Pratiwi Himpunan Mahasiswa Fisika FMIPA UNILA
  • Arif Surtono University of Lampung
  • Sri Wahyu Suciyati University of Lampung

DOI:

https://doi.org/10.23960/jemit.v3i1.88

Keywords:

Salt bridge, Electrical characteristics, Acid zinc solution, Voltaic cell

Abstract

The research was conducted to analyze the effect of variations in pH of acid zinc solution in two compartment voltaic cells with Cu(Ag)-Zn electrodes on the value of electrical characteristics and the resulting corrosion rate. The Cu(Ag)-Zn pair is used to generate voltage and current in the cell with seawater electrolyte and zinc acid solution. The two compartments are lined with salt bridge made from mixture of Al2O3 (aluminum oxide), NaCl (seawater) 1 mole concentration dissolved in “tiga roda” white cement. The voltaic cell consisted of 5 cells arranged in series circuit, for each cell at the cathode (Cu(Ag)) containing ± 250 ml seawater and at the anode (Zn) containing ± 200 ml cid zinc solution which was varied with a pH of 4.5 and 6. The voltaic cell was measured with multitester every 1 hour for 3 days. Based on the research that has been done, it can be concluded that by using an acid zinc electrolyte solution which has a lower pH value, it will increase the value of the electrical characteristics and increase the corrosion rate produced by voltaic cell.

Downloads

Download data is not yet available.

References

Amanto, H. dan Daryanto. (1999). Ilmu Bahan. Jakarta: Bumi Aksara.

Ansari, I., Indra, B. W., Nurohmahwati, F., dan Zakaria, I. (2017).Pengaruh Waktu dan Luas Permukaan Terhadap Ketebalan Produk Pada Elektroplating Acid Zinc. Jurnal Teknik kimia. Tanggerang Selatan: Universitas Pamulang. 1(1), 1-6.

Badea, G. E., Corbu, I., Caraban, A., dan Cret. P. (2007). Seawater Electrolysis for Hydrogen Production. Revue Roumaine de Chimie. (54)1, 55-61.

Einar, B. (2003). Corrosion and Protection. Norway: Springer.

Kholiq, I. (2015). Pemanfaatan Energi Altenatif Sebagai Energi Terbarukan untuk Mendukung Subtistusi BBM. Jurnal IPTEK. 19(2), 71-91.

Kuwahara. (2001). Geologi laut. Jakarta: Erlangga.

Nurbani, M. P. (2018). Analisa Pengaruh pH Terhadap Laju Korosi Baja S45c Hasil Galvanisasi Celup Panas Dengan Metode Kehilangan Berat. Skripsi. Jakarta: Universitas Trisakti.

Nybakken, J. W. (1992). Biologi Laut, Suatu Pendekatan Ekologis. Jakarta: PT. Gramedia Pustaka.

Pangestu, S. S. (2018). Analisis Laju Korosi Pada Sistem Energi Listrik Alternatif Berbasis Elektrolit Air Laut. JURNAL Teori dan aplikasi fisika. 6(1), 11-19.

Pauzi, G. A., Arwaditha, R. K., dan Supriyanto, A. (2017). Desain dan Realisasi Akumulator Elektrolit Air Laut Dengan Penambahan Sodium Bicarbonate (NaHCO3) Sebagai Sumber Energi Alternatif. JURNAL Teori dan aplikasi fisika. 8(2), 78-82.

Pauzi, G. A., Anwar, S., Supriyanto, A., dan Suciyati, S. W. (2021). Analisis Jembatan Garam Campuran Alumina dan Kalsium Karbonat Pada Karakteristik Elektrik Pembangkit Listrik Sel Galvanis dengan Elektrolit Air Laut. Journal of Energy, Material and Instrumentation Technology. 2(4), 78-85.

Pauzi, G. A., Hudaya, E., Supriyanto, A., Warsito, dan Surtono, A. (2016). Analisis Uji Karakteristik Elektrik Air Laut Sebagai Sumber Energi Listrik Terbarukan. Prosiding Seminar Nasional Sains Matematika Informatika dan Aplikasinya IV. 4, 1-8.

Purnomo. (2010). Pengaruh Keasaman Buah Jeruk Terhadap Konduktivitas Listrik. ORBITH. 6(2), 276-281.

Vlack, L.H. (1992). Ilmu dan Teknologi Bahan (Ilmu Logam dan Bukan Logam).Diterjemahkan oleh Sriati Djaprie, M.E., M.Met. Jakarta: Erlangga.

Wicaksono, D., Bhakti, T. L., Taruno, R. B., Subroto, M. R. S., dan Mustikasari, A. (2021). Sistem Sensor Untuk Pemantauan Kadar Oksigen Terlarut Berbasis Galvanic Pada Kolam Budidaya Ikan Air Tawar. Jurnal Teknologi dan Sistem Komputer. 9(2), 83-89.

Winston, R. R. (2008). Corrosion And Corrosion Control An Introduction To Corrosion Science And Engineering Fourth Edition. A John Wiley & Sons, Inc.

Yulianti, D., Supriyanto, A., dan Pauzi, G. A. (2017). Analisis Kelistrikan Sel Volta Memanfaatkan Logam Bekas. Jurnal Teori dan Aplikasi Fisika. 5(1), 49-57.

Downloads

Published

2022-02-19

Issue

Vol. 3 No. 1 (2022): Journal of Energy, Material, and Instrumentation Technology

Section

Articles

License

Copyright (c) 2022

Creative Commons License

This work is licensed under a Creative Commons Attribution 4.0 International License.