Pengaruh Inhibitor Ekstrak Daun Inai (Lawsonia inermis L) Terhadap Laju Korosi Baja St37 dalam Larutan HCl 3%
DOI:
https://doi.org/10.23960/jemit.v2i3.147Keywords:
Henna leaves extract, St37 carbon steel, HCl, XRD, SEM-EDSAbstract
Henna leaves extract (Lawsonia inermis L) is used as a corrosion inhibitor in St37 steel soaked in 3% HCl corrosive medium. To find out the effect of inhibitor concentration on the corrosion rate of steel, the variation of inhibitor concentration is 0, 3, 5, 7 and 9%. Corrosion rate testing is done by mass loss method. Corrosion rate was tested on low carbon steel with and without inhibition of henna extract for 6 days. The results showed that the greater the concentration of inhibitor of henna extract used, the corrosion rate would decrease and the ability to inhibit corrosion would increase. The greatest corrosion efficiency occurred at a concentration of 9% with an efficiency of 88.84%. The results of X-Ray Diffraction (XRD) characterization showed that the phase formed was pure iron (Fe). Secondary Electron Microscopy (SEM) characterization showed uneven clusters and smaller sizes, holes and cracks were also less with the addition of inhibitory leaves extract than without the addition of inhibitory leaves extract. This result is reinforced by the percentage of corrosion products shown in the results of the characterization of Energy Dispersive Spectroscopy (EDS).
Downloads
References
Anggaretno, G. (2012). Analisa Pengaruh Jenis Elektroda terhadap Laju Korosi pada Pengelasan Pipa API 5L Grade X65. Jurnal Teknik ITS.
G, A. S. (2017). Efektifitas Ekstrak Daun Sirsak sebagai Inhibitor pada Baja Karbon Api 5L dalam Larutan NaCl 3 %. Jurnal Teori Dan Aplikasi Fisika.
Handani, S., Wildani, S., & -, E. (2015). Pengaruh Inhibitor Ekstrak Daun Inai (Lawsonia Inermis) Terhadap Laju Korosi Baja ST. 37 Diukur dengan Metode Pengurangan Massa. Jurnal Riset Kimia. https://doi.org/10.25077/jrk.v4i1.148
Ilim, & Hermawan, B. (2008). Study Penggunaan Ekstrak Buah Lada, Buah Pinang dan Daun Teh sebagai Inhibitor Korosi Baja Lunak dalam Air Laut Buatan yang Jenuh Gas CO_2. Prosiding Seminar Nasional Sains Dan Teknologi II.
Ishak, I. (2016). Kinerja Inhibitor Na2CrO4 Dalam Larutan NaCl Untuk Melindungi Baja Tahan Karat Austenitik Tersensitisasi Dari Serangan SCC. Jurnal Sains Dan Teknologi Reaksi. https://doi.org/10.30811/jstr.v2i1.63
Laju, S., Morfologi, S., Putri, A. M., & Rochani, I. (2012). Studi Laju Korosi dan Surface Morfologi Pipa Bawah Laut API 5L Grade X65 dengan Variasi Sudut Bending. Jurnal Teknik ITS.
Mardina, D. (2018). Efektivitas Ekstrak Daun Jambu Biji (Psidium Guajava Linn) Sebagai Inhibitor Pada baja Karbon St37 Dalam Medium Korosif NaCl 3%. Universitas Lampung.
Meryanalinda, A. R. (2014). Perhitungan dan Analisis Laju Korosi. Laju Korosi.
Sanjaya, R., Ginting, E., & Riyanto, A. (2018). Efektivitas Ekstrak Daun Pepaya (Carica papaya l) sebagai Inhibitor pada Baja ST37 dalam Medium Korosif NaCl 3% dengan Variasi Waktu Perendaman. Jurnal Teori Dan Aplikasi Fisika. https://doi.org/10.23960/jtaf.v6i2.1839
Sari, D. M., Handani, S., & Yetri, Y. (2013). Pengendalian Laju Korosi Baja St-37 dalam Medium Asam Klorida dan Natrium Klorida Menggunakan Inhibitor Ekstrak Daun Teh (Camelia sinensis). Jurnal Fisika Universitas Andalas.
Trethewey, K. R and Chamberlain, J. (1991). Korosi untuk Mahasiswa dan Rekayasa. In Jurnal Matematika Dan Sains.
Udianto, a N. B., Urwantini, K. R. P., Ujitno, B. a T. J. S., Babarsari, J., Pos, K., & Yogyakarta, Y. (2009). Antar Butir Dari Material Baja Tahan Karat Austenitik Setelah Mengalami Proses Pemanasan Material Karat Structure Observation of. Jfn, 3(2), 107–130.